Tungsten Carbide Bearings

The standard bearing used is a Carbon-Graphite compound which has excellent corrosion resistant characteristics when operating in most liquid environments.
Certain fluids will attack the binder or process streams may contain abrasive solids which preclude the use of carbon-graphite bearing. In these cases alternate materials are available such as:

• Silicon Carbide
• Carbon-Graphite
• Aluminum Oxide (ALOX)
  

 

A brief description of each of these bearing materials

CARBON-GRAPHITE

These are materials manufactured from a blending of Carbon and
Graphite powders with a hydrocarbon binder. The result is a materials which is resistant to wear, chemically resistant and thermally stable. There are many grades of Carbon-Graphite bearing materials. The shaft journal treatments M-2, M-3 or NCB can be used with type B bearings although it is not
necessary. Journal treatment will extend the life of the shaft since it will resist abrasion if the bearings run dry or are exposed to abrasive particles. See Engineering data sheet 26E for more informationconcerning shaft coatings.
when a bearing wear detector is used，the maximum fluid temperature for a sleeved, bearing is 400°F.


SILICON CARBIDE

- This material is a self sintered, high density hardened material with very good wear and chemical resistance. Silicon carbide is very wear resistance but care must be taken when applying this material because silicon carbide is brittle making it susceptible to thermal and mechanical shock. This type of bearing is much less forgiving than carbon graphite when system upsets, such as dry running and cavitation, occur. Silicon graphite bearings do not wear gradually. If the bearings fail they normally shatter into many pieces causing a catastrophic failure. CARBON-GRAPHITE - This is a grade of Carbon-Graphite which is used primarily in
Hydrofluoric Acid service. Experience has shown that the binder of the carbon graphite type B
bearings is attacked by hydrofluoric acid causing the bearing to swell and seize on the shaft. The type
F-2 graphite composition is inert to hydrofluoric acid attack.
This grade can be used on other applications, but most are covered by the Type B bearing which is less expensive and more readily available.
run dry or are exposed to abrasive particles. See Engineering data sheet 26E for more information
concerning shaft coatings.

If you are interested in our products, please feel free to contact by e-mail: sales@chinatungsten.com，or telephone: 0086 0592 5129696。